PA T is a hemihydrate plaster (CaSO4 * 1/2 H2O) produced from naturally occurring gypsum mineral.
This product is used in the ceramics industry to produce working moulds for ram press machines
Technical Information
Plaster to Water Ratio | |
Plaster to water ratio | 3,00:1 |
Water / plaster ratio (%) | 33 |
Plaster / water mix ratio (by weight) | 3.00: 1 |
Setting Parameters | |
Schimidth / Vicat Ring Fluidity (mm) | 190 – 250 |
Initial Setting Time (minute) | 10 – 20 |
Fina Setting Time (minute) | 15 – 30 |
Linear Expansion (%) | mak. 0,20 |
Mechanical Properties | |
Average Dry Flexural Strength (kg/cm2) | 90 |
Average Dry Compressive Strength (kg/cm2) | 350 |
Physical Properties | |
Particle size (% weight retained) | 200 μm: <0,04 % |
Packaging and Shelf Life
| Packing | Shelf Life (Month) |
Bigbag (Ton) | 1,0 | 6 |
Kraft Bags(kg) | 25 | 6 |